PO FA Potable Water & Food Contact Approved
- Description
- APPLICATION AREAS
- FEATURES
- TECHNICAL PROPERTIES
- PACKAGE
- TDS
Description
Po Fa Potable Water & Food Contact Approved is a very fast curing, two component, aromatic, flexible, pure polyurea system coating derived from a reaction of an isocyanate prepolymer and an amine terminated resin blend. This product has been approved for potable water & food contact and especially designed waterproofing for potable water tanks and pipes. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment.
- Potable water storage facilities and tanks
- Potable water pipes
- Food production and processing plants
- Food storage tanks
- Rain storage facilities and sedimentation tanks
- Filtration systems
- Swimming pools and aquariums
- Approved for potable water & food contact
- Fast reactivity and fast return to service time
- 100% solid, VOC free, no solvents
- Environmentally friendly
- Very good tensile and structural strength
- Excellent chemical resistance
- Excellent impact and abrasion resistance
- Excellent adhesion on concrete, steel, aluminum, plastics, fibers, wood, foam etc.
- Excellent flexibility
- Excellent crack bridging properties
- Temperature and moisture insensitive
- Excellent corrosion protection
- UV, chlorine and saltwater resistant
- Variable application thickness is possible
- Transparent
| COMPONENT PROPERTIES | ||||
|---|---|---|---|---|
| UNIT | METHOD | ISO COMPONENT (A | AMINE COMPONENT(B) | |
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
| Shelf life | - | - | 9 months | 9 months |
| PROCESS PROPERTIES | ||||
| UNIT | DATAS | |||
| Mix Ratio | By volume | A=100 B=100 | ||
| Mix Ratio | By weight | A= 112 B= 100 | ||
| Process temperature(°C) | °C | A: 70-80 B: 70-80 | ||
| Process pressure (bar) | Bar | A: 180-200 B: 180-200 | ||
| PHYSICAL PROPERTIES | ||||
| UNIT | DATAS | |||
| Chemical structure | A: MDI Prepolymer B: Amine Resin | |||
| VOC content (%) | ASTM D1259 | 0 | ||
| Solid content (%) | ASTM D2697 | 100 | ||
| Gel time (sec) | -- | 5-10 | ||
| Tack free time (sec) | -- | 15-30 | ||
| Recoat time (hr) | -- | 0-12 (without pre-treatment) | ||
| Post cure time (hr) | -- | 24 | ||
| Density (gr/cm3) | ASTM D792 | 0,99-1,03 | ||
| Tensile strength (MPa) | ASTM D638 | ≥ 18 | ||
| Modulus (MPa) | ASTM D638 | %100 elongation ≥10 %300 elongation ≥15 | ||
| Elongation at break (%) | ASTM D638 | ≥350 | ||
| Hardness (Shore D) | ASTM D2240 | 40-45 | ||
| Tear strength (N/mm) | ASTM D 624 | ≥50 | ||
| Impact resistance | EN ISO 5470-1 | Class III | ||
| Thermal Resistance | - | -30 °C-100°C | ||
| Pull off strength (N/mm2) | ASTM D 4541 | Concrete: ≥2,5 Steel: ≥6 | ||
| Approval to food contact | EN 1186-1/15 | Suitable |