Po Fx Enhanced Flexibility
- Description
- APPLICATION AREAS
- FEATURES
- TECHNICAL PROPERTIES
- PACKAGE
- TDS
Description
PO FX Enhanced Flexibility is a very fast curing, two component and elastomeric pure polyurea system. In addition to having basic properties of polyurea systems properties, it has a lot more elasticity to be able to use where elasticity is essential like in metal roof and geotextile coatings. It can be used with confidence in both interior and exterior applications. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment.
- Pools and storage tanks
- Roofs, terraces and garages
- Geotextile coating
- Decorative applications
- Water and amusement parks
- Excellent flexibility and elongation
- Fast reactivity and fast return to service time
- Seamless coating
- 100% solid, VOC free, no solvents
- Environmentally friendly
- Very good tensile and structural strength
- Excellent adhesion on concrete, steel, aluminum, plastics, fibers, wood, foam etc.
- Excellent flexibility
- Excellent crack bridging properties
- Temperature and moisture insensitive
- UV, chlorine and saltwater resistant
- Variable application thickness is possible
- Broad color spectrum
| COMPONENT PROPERTIES | ||||
|---|---|---|---|---|
| UNIT | METHOD | ISO COMPONENT (A | AMINE COMPONENT(B) | |
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
| Shelf life | - | - | 9 months | 9 months |
| PROCESS PROPERTIES | ||||
| UNIT | DATAS | |||
| Mix Ratio | By volume | A=100 B=100 | ||
| Mix Ratio | By weight | A= 112 B= 100 | ||
| Process temperature(°C) | °C | A: 70-80 B: 70-80 | ||
| Process pressure (bar) | BAR | A: 180-200 B: 180-200 | ||
| PHYSICAL PROPERTIES | ||||
| METHOD | DATA | |||
| Chemical structure | A: MDI Prepolymer B: Amine Resin | |||
| Color | White, black, grey, yellow and any RAL color | |||
| VOC content (%) | ASTM D1259 | 0 | ||
| Solid content (%) | ASTM D2697 | 100 | ||
| Gel time (sec) | - | 20-30 | ||
| Tack free time (sec) | - | 60-90 | ||
| Recoat time (hr) | - | 0-12 (without pretreatment) | ||
| Post cure time (hr) | - | 24 | ||
| Density (gr/cm3) | ASTM D792 | 0,99-1,03 | ||
| Tensile strength (MPa) | ASTM D638 | ≥ 10 | ||
| Modulus (MPa) | ASTM D638 | %100 elongation ≥10 %300 elongation ≥15 | ||
| Elongation at break (%) | ASTM D638 | ≥500 | ||
| Hardness (Shore D) | ASTM D2240 | 70-75 | ||
| Pull off strength (N/mm2) | ASTM D 4541 | Concrete: ≥2 Steel: ≥6 |
| Type | Volume | Box |
|---|---|---|
| - | 200 kg | 1 |
| - | 225 kg | 1 |