FWA Fast Cure PU Windshield Adhesive
One component, moisture curing polyurethane based adhesive for direct glazing in AUTOMOTIVE GLASS REPLACEMENT.
- Description
- Application Areas
- Features
- TECHNICAL PROPERTIES
- PACKAGE
- TDS
Description
Fast Cure PU Windshield Adhesive is single part polyurethane based, high modulus sealant, which cures on exposure to atmospheric moisture to form elastomeric mastic. Fast Cure PU Windshield Adhesive has excellently water-proof, high bonding strength, oil resistant, aging resistant, salt fog resistant, and can bear long time vibration. Fast Cure PU Windshield Adhesive offers excellent adhesion on glass and metal, it is most suitable for bonding windshield in the automotive industry
- It is especially useful in bonding windshield glass into automotive frames.
- One component formulation.
- Good non-sag properties.
- Short cut-off string.
- Cold application.
- Fast curing – Rapid strength development.
- High mechanical performance.
- High Modulus.
- High initial bond strength.
- Can be overpainted.
| Before Curing | ||
|---|---|---|
| Basis | Polyurethane | |
| Consistency | Thixotropic | |
| Curing Mechanism | Moisture Curing | |
| Density | 1,35±0,05 g/ml | |
| Curing Rate | approx. 4 mm/24 h | |
| Tack Free Time | 30±10 min. (23°C and 50% R.H) | |
| Extrudability, ml/min. | ≥70 | |
| Sagging | 0 mm | (EN ISO 7390) |
| After Curing | ||
| Hardness Shore A | 45-60 | After 7 days |
| Paintibility | Yes* | |
| Elongation at break | Min. 400% | (ASTM D412) |
| Tensile Strength | Min. 4.5 MPa | (ASTM D412) |
| Tensile Shear Strength | Min. 2.5 MPa | |
| Drop Degree, MM | 0 | |
| Solid Content | ≥94 |
| Type | Volume | Box |
|---|---|---|
| Black | 300 ml | 12 |
| Black | 600 ml | 12 |